How to Weld – Page 13 – www.materialwelding.com

AISI 8630 Welding Procedure AISI 8630, or commonly called 8630 alloys, is a low alloy steel alloyed with Nickel, chromium, molybdenum, and chromium compared to AISI 4140 (AISI 4140 Welding Procedure) that lacks Nickel. AISI 8630 has high tensile strength, yield strength, and good toughness making it a good material for hot forging & rolling. AISI 8630 is used for making gears, shafts, crankshafts & valves for various industries. Material Specification for supply for AISI 8630 The UNS number of AISI 8630 is UNS G86300. AISI 8630 material specifications are ASTM A752, A829, A331, A513, A519, AMS 6281, AMS 6530. Complete details of AISI 8630 material specifications are given in the below table: Chemical composition of AISI 8630 AISI 8630 chemical compositions are listed below for reference: Iron remainingManganese: 0.65-0.95Chromium: 0.4-0.6Nickel: 0.35-0.75Carbon: 0.28-0.33Silicon: 0.15-0.30Molybdenum: 0.15-0.25Sulfur: ≤ 0.040Phosphorus: ≤ 0.035 Carbon Equivalent for steel, low alloy, C-Mn steel and cast iron Mechanical properties of AISI 8630 The minimum tensile strength of AISI 8630 is 90 Ksi & Yield strength is 79.8 Ksi. AISI 8630 hardness is 15HRC (217HV). Weldability of AISI 8630 AISI 8130 is having a High Carbon Equivalent along with high strength which makes it prone to weld and HAZ cracking. Stringent control on Welding Preheat is required to avoid any weld cracking issue. Post heating after welding is very beneficial to controlling delayed cracking by allowing hydrogen diffusion. Types of Crack in welding and crack prevention After completion of the welding, the welded part shall be allowed to slow cool thus preventing the formation of martensite in the weld and Heat Affected Zone (HAZ). AISI 8630 due to high carbon content & other alloying elements are prone to martensite formation if the cooling rate is high during weld solidification. Welding electrode/ filler wire for welding AISI 8630 Stick Welding or SMAW of AISI 8630 shall be carried out using stick welding rod E10018-D2 (AWS A5.5). The welding rod must be baked properly before use. Always use low hydrogen welding electrodes for welding of AISI 8630 material. Properly baked/ reconditioned stick welding rods ensure a low level of dissolved hydrogen in weldment and prevent the hydrogen cracking that can occurs in AISI 8630 weldment & HAZ. What is Low Hydrogen electrodes, Their Storage & Baking Procedure? TIG or MIG-MAG welding of AISI 8630 shall be carried out using the filler rod ER100S-G. ER100S-G is a high-strength solid wire filler rod. To ensure a sound and crack-free weld with ER100S-G, preheat the parts before welding and maintain the preheat temperature during the welding. Preheat/ Interpass for AISI 8630 For welding of AISI 8630 material, apply a minimum Preheat temperature of 500°F or 250°C. This preheat temperature must be applied to prevent the formation of martensite in the weldment and Heat Affected Zone (HAZ). You can use our ONLINE PREHEAT CALCULATOR to find preheat temperature for any material based on its chemical composition. If arc air gouging is the preparation method to be used for AISI 8630, then Preheating before gouging must be exercised. Preparation for welding by re-machining or grinding does not require preheating as they are mostly cold material cutting processes and will not produce any microstructural changes. Stress-relief, PWHT of AISI 8630 Post Weld Heat Treatment or Stress relieving PWHT after welding for AISI 8630 material shall be carried out at 1200°F (650°C). Holding time usually based on thickness shall be 1 hour/inch. For an application requiring hardness control such as NACE requirements, holding time can be up to 4 hours to meet the 250HV limit. Heat Treatment for AISI 8630 Annealing: if required for improved machining material, it is good to have a coarse pearlite microstructure with a minimum amount of ferrite. This can be achieved by austenitizing at a temperature of 1550°F (845°C) and furnace cooling to a temperature of 1350°F (730°C) then to 1180°F (640°C) at a cooling rate of 20°F/hr. Normalizing: Normalizing at a temperature of 1600°F (870°C) followed by cooling in the air. Hardening: Austenitise the 8630 at a temperature around 1525 °F to 1600°F (830 – 870°C) and followed by water or oil quenching. Tempering: To be followed by quenching. Similar Posts How to Weld EN24/ AISI 4340 (DIN 34CrNiMo6) and EN 24/4340 with A36 or carbon steel?AISI 8620 (21NiCrMo2) welding procedure & guidelinesHow to Weld AISI 4145Difference between Annealing and normalizing of steel